Influence of Structure Directionality on Fatigue Properties of Formed Al Alloy.
Jíša, David ; Mazal, Pavel (referee) ; Liškutín, Petr (advisor)
The main goal of this diploma thesis is the examination of the influence of structure directionality on fatigue properties of formed aluminium alloy 6082/T6. The main attention is focused on the study of the influence of structure directionality on kinetics of short fatigue cracks growth. The measurement of short fatigue cracks growth was performed on cylindrical samples. The samples were made in two different directions; one parallel with the forming direction and second perpendicular to the forming direction. Servo hydraulic machine MTS 880 was used for the cyclic loading. The samples were cycled at two different constant stress amplitudes. Cyclic loading was systematically interrupted in order to measure the length of short cracks by a light microscope. Tensile tests, measuring of cycling hardening-softening curves, observation of microstructure, observation of surface relief, measuring of microhardness and fractographical analysis of fracture surfaces were used for further examination of the influence of the structure directionality. Some of these measured characteristics did not show any influence of the structure directionality (microhardness, fatigue life curve, Young modulus). In other cases is this influence measurable, however insignificant (yield stress, ultimate stress, cyclic hardening-softening curves and kinetics of short fatigue cracks growth). It can be summarised that the material, though the directionality of its microstructure is apparent, shows relatively isotropic mechanical behaviour.
|
|
|
Microstructure, it´s Stability and Fatigue Properties of Ultra-Fine Grained Copper Prepared by ECAP Method
Navrátilová, Lucie ; Konečná, Radomila (referee) ; Obrtlík, Karel (referee) ; Kunz, Ludvík (advisor)
This work deals with fatigue properties and stability of microstructure of ultrafine-grained (UFG) copper prepared by severe plastic deformation by means of equal channel angular pressing (ECAP) method. The effect of different fatigue loading regimes and thermal exposition on microstructural changes was investigated and the fatigue lifetime curves were experimentally determined. The research attention was focussed on localization of cyclic plastic deformation and fatigue crack initiation in UFG structure. Experimental results indicate that after stress-controlled fatigue loading (both symmetrical and asymmetrical) the microstructure remains ultrafine; no grain coarsening was observed. Contrary to this, strain-controlled fatigue loading results in formation of bimodal structure. Grain coarsening was observed also after thermal exposition at 250 °C for 30 minutes. Annealing at lower temperatures does not result in grain coarsening or development of bimodal structure. Fatigue loading results in development of surface relief in form of cyclic slip markings. Their density, distribution and shape differ for particular fatigue loading regimes. Differences in crack initiation mechanism in low- and high-cycle fatigue region were found. Nevertheless, the characteristic feature for all loading regimes was stability of UFG microstructure in the region of cyclic slip bands and fatigue cracks.
|
|
|
Microstructure, it´s Stability and Fatigue Properties of Ultra-Fine Grained Copper Prepared by ECAP Method
Navrátilová, Lucie ; Konečná, Radomila (referee) ; Obrtlík, Karel (referee) ; Kunz, Ludvík (advisor)
This work deals with fatigue properties and stability of microstructure of ultrafine-grained (UFG) copper prepared by severe plastic deformation by means of equal channel angular pressing (ECAP) method. The effect of different fatigue loading regimes and thermal exposition on microstructural changes was investigated and the fatigue lifetime curves were experimentally determined. The research attention was focussed on localization of cyclic plastic deformation and fatigue crack initiation in UFG structure. Experimental results indicate that after stress-controlled fatigue loading (both symmetrical and asymmetrical) the microstructure remains ultrafine; no grain coarsening was observed. Contrary to this, strain-controlled fatigue loading results in formation of bimodal structure. Grain coarsening was observed also after thermal exposition at 250 °C for 30 minutes. Annealing at lower temperatures does not result in grain coarsening or development of bimodal structure. Fatigue loading results in development of surface relief in form of cyclic slip markings. Their density, distribution and shape differ for particular fatigue loading regimes. Differences in crack initiation mechanism in low- and high-cycle fatigue region were found. Nevertheless, the characteristic feature for all loading regimes was stability of UFG microstructure in the region of cyclic slip bands and fatigue cracks.
|
|
|
Influence of Structure Directionality on Fatigue Properties of Formed Al Alloy.
Jíša, David ; Mazal, Pavel (referee) ; Liškutín, Petr (advisor)
The main goal of this diploma thesis is the examination of the influence of structure directionality on fatigue properties of formed aluminium alloy 6082/T6. The main attention is focused on the study of the influence of structure directionality on kinetics of short fatigue cracks growth. The measurement of short fatigue cracks growth was performed on cylindrical samples. The samples were made in two different directions; one parallel with the forming direction and second perpendicular to the forming direction. Servo hydraulic machine MTS 880 was used for the cyclic loading. The samples were cycled at two different constant stress amplitudes. Cyclic loading was systematically interrupted in order to measure the length of short cracks by a light microscope. Tensile tests, measuring of cycling hardening-softening curves, observation of microstructure, observation of surface relief, measuring of microhardness and fractographical analysis of fracture surfaces were used for further examination of the influence of the structure directionality. Some of these measured characteristics did not show any influence of the structure directionality (microhardness, fatigue life curve, Young modulus). In other cases is this influence measurable, however insignificant (yield stress, ultimate stress, cyclic hardening-softening curves and kinetics of short fatigue cracks growth). It can be summarised that the material, though the directionality of its microstructure is apparent, shows relatively isotropic mechanical behaviour.
|